Electro Galvanized Wire Description
Electro galvanized wire is made of high quality low carbon steel wire rod as raw material, with more than 25 years producing experience and quality first philosophy, our galvanizing layer is homogeneous solid, corrosion resistance and anti-rust, wire is high level flexibility and softness .
We supply galvanized steel wire, fence wire, spring wire, cable tie and metal wire mesh for construction. Galvanized iron wire is made of low-carbon steel bar after being hard drawn and galvanized. Electro Galvanized Wire is provided in the form of coil, bobbin, cutting wire, loop wire or U-shaped wire. The galvanized layer is different according to specific requirements. Galvanized iron wire is sometimes simplified to GI wire.
Electro Galvanized Wire is also called cold galvanized wire. Put the low carbon steel wire into the electroplating tank, and slowly galvanize the metal surface through the unidirectional current. The speed of zinc on electrogalvanized wire is slow, and the thickness is only hot-dip galvanized wire,one tenth.
Cold galvanized wire is a unidirectional current in the electroplating bath. The surface of the iron wire is gradually electroplated. The production speed is slow, the coating is uniform, and the thickness is generally 3-15 microns. It has bright appearance, anti-rust and decorative properties. Keep tightly closed in a cool place for up to 18 months. And can provide customized services according to customer requirements, contact us for more information!
|name:||Electro Galvanized Wire|
|Wire diameter range||Bwg25-Bwg6(0.5mm-5.0mm)|
|Packing||100g/coil-1000kgs/coil, plastic inside and hessian outside or plastic inside and plastic woven bag outside, pallet can be used according to customers' request|
1. Thick zinc layer, fine crystals, uniformity and no porosity, good corrosion resistance;
2. The zinc layer obtained by electroplating galvanized wire is relatively pure, corrodes slowly in the mist of acid, alkali, etc., and can effectively protect the steel substrate;
3. The zinc coating is passivated by chromic acid to form white, colorful, military green, etc., which is beautiful and decorative;
4. Because the coating of electro-galvanized wire has good ductility, it can be formed by cold punching, rolling, bending and other methods without damaging the coating.
Mainly used for processing electro-galvanized twisted wire mesh, electro-galvanized crimped wire mesh, electro-galvanized hexagonal wire mesh, electro-galvanized diamond wire mesh, electro-galvanized chain link fence, electro-galvanized welded wire mesh, electro-galvanized fence, electro-galvanized fence, electro-galvanized gabion mesh , Electro-galvanized steel wire mesh, electro-galvanized iron wire, electro-galvanized filter and other wire mesh products. It can also be used in communication equipment, medical equipment and electric brushes, steel cables, filters, high-pressure pipelines, construction, handicrafts and other industries. And Widely used on construction project as binding wire, mesh weaving, hanging etc.
Hot Dipped Galvanzied Wire is made by hot-dip galvanizing process, an effective metal anti-corrosion method, mainly used in metal structure facilities in various industries. The derusted steel parts are immersed in a molten zinc solution at about 500°C, so that a zinc layer is attached to the surface of the steel parts, so as to achieve the purpose of corrosion protection.
Electro Galvanized Wire is made by electro galvanizing, also known as cold galvanizing process, which uses electrolysis to form a uniform, dense, and well-bonded metal or alloy deposition layer on the surface of the part. Compared with other metals, zinc is a relatively cheap and easy to plate metal. It is a low-value anti-corrosion electroplating layer, which is widely used to protect steel parts, especially to prevent atmospheric corrosion and decoration.
Hot Dipped Galvanzied Wire process flow
Finished product pickling-water washing-adding booster solution-drying-rack plating-cooling-dosing-cleaning-polishing-hot-dip galvanizing.
Electro Galvanized Wire process flow
Chemical degreasing-hot water washing-water washing-electric degreasing-hot water washing-water washing-strong corrosion-water washing-electrogalvanized iron alloy-water washing-water washing-luminescence-passivation-water washing-drying.
There are many processing techniques for Hot Dipped Galvanzied Wire.
After degreasing, pickling, dipping, and drying, the workpiece is immersed in a molten zinc bath and raised for a certain period of time to make it hot-dip galvanized. Some hot-dip pipe fittings are processed in this way.
Electro Galvanized Wire is processed by electrolytic equipment.
After degreasing, pickling and other processes, it is immersed in a solution containing zinc salt, connected to electrolysis equipment, and deposited on the workpiece during the directional movement of the positive and negative electrodes.
The overall appearance of Hot Dipped Galvanzied Wire is slightly rough, which will produce process water lines, dripping tumors, etc., especially at one end of the workpiece, the overall appearance is silvery white.
The surface of Electro Galvanized Wire is relatively smooth, mainly yellow-green, of course, there are also colorful, blue-white, white and green light. There is basically no zinc tumor, agglomeration, etc. in the entire workpiece.